High-Strength Brazing Alloys for Copper
SKU |
Composition of SIlver |
Composition of Copper |
Composition of Cadmium |
Composition of Phosphorous |
Width |
Diameter |
Height |
Melting Temperature |
Braze Type |
Length |
Pkg.Qty. |
FCG_15V10 |
15% |
80% |
0% |
5% |
--- |
3.18mm |
--- |
1190° to 1480° |
Flux Required |
457.2mm |
16 |
x
High-Strength Brazing Alloys for Copper
Estimated Delivery - 15 to 17 days
|
FCG_15V09 |
15% |
80% |
0% |
5% |
--- |
3.18mm |
--- |
1190° to 1480° |
Flux Required |
457.2mm |
4 |
x
High-Strength Brazing Alloys for Copper
Estimated Delivery - 15 to 17 days
|
FCG_15V08 |
15% |
80% |
0% |
5% |
--- |
2.38mm |
--- |
1190° to 1480° |
Flux Required |
457.2mm |
29 |
x
High-Strength Brazing Alloys for Copper
Estimated Delivery - 15 to 17 days
|
FCG_15V07 |
15% |
80% |
0% |
5% |
--- |
2.38mm |
--- |
1190° to 1480° |
Flux Required |
457.2mm |
7 |
x
High-Strength Brazing Alloys for Copper
Estimated Delivery - 15 to 17 days
|
FCG_15V06 |
15% |
80% |
0% |
5% |
--- |
1.59mm |
--- |
1190° to 1480° |
Flux Required |
508mm |
50 |
x
High-Strength Brazing Alloys for Copper
Estimated Delivery - 15 to 17 days
|
FCG_15V05 |
15% |
80% |
0% |
5% |
--- |
1.59mm |
--- |
1190° to 1480° |
Flux Required |
508mm |
12 |
x
High-Strength Brazing Alloys for Copper
Estimated Delivery - 15 to 17 days
|
FCG_15V04 |
15% |
80% |
0% |
5% |
--- |
1.59mm |
--- |
1190° to 1480° |
Flux Required |
457.2mm |
67 |
x
High-Strength Brazing Alloys for Copper
Estimated Delivery - 15 to 17 days
|
FCG_15V03 |
15% |
80% |
0% |
5% |
--- |
1.59mm |
--- |
1190° to 1480° |
Flux Required |
457.2mm |
16 |
x
High-Strength Brazing Alloys for Copper
Estimated Delivery - 15 to 17 days
|
FCG_15V02 |
15% |
80% |
0% |
5% |
3.18mm |
--- |
1.27mm |
1190° to 1480° |
Flux Required |
508mm |
28 |
x
High-Strength Brazing Alloys for Copper
Estimated Delivery - 15 to 17 days
|
FCG_15V01 |
15% |
80% |
0% |
5% |
3.18mm |
--- |
1.27mm |
1190° to 1480° |
Flux Required |
508mm |
7 |
x
High-Strength Brazing Alloys for Copper
Estimated Delivery - 15 to 17 days
|